Research Article

Electrochemical and structural characterization of nickel oxide filled activated carbon for upercapacitor electrode application

Ahmed T. O.1*, Ogunleye O. O.1, Galadima I. A.2, Sulle B. A.2, Bello A.3
1 Department of Physics, Federal University, Lokoja, Kogi State
2 Department of Physics, Ahmadu Bello University, Zaria
3 Department of Physics, Faculty of Natural and Agricultural Science, University of Pretoria, South Africa
* Corresponding author: tajudeen.ahmed@fulokoja.edu.ng
Published: Jun, 2016
Pages: 7-15

Abstract

We have demonstrated that activated carbon could be produced via microwave-assisted activation at a much shorter time (ranging from 2-5 min) and reduced cost compared to the conventional activation method embraced by most researchers in the production of activated carbon. The research work is not only limited to surface chemistry and adsorption studies but also includes structural, microstructural and electrochemical studies/investigations of the produced Nickel Oxide Filled Activated Carbon (NOFAC). Its uniqueness is tied to cost effectiveness and the use of agricultural waste product. Activated carbon filled with nickel oxide was prepared via microwave-assisted chemical activation using coconut shell, palm kernel shell and their mixture with potassium hydroxide as activating agent. The effect of the incorporation of NiO on the structure and surface chemistry of the raw materials after activation was studied employing Fourier Transform Infra-Red (FTIR) Spectroscopy, Transmission Electron Microscopy (TEM) and X-ray Diffraction (XRD) analysis. The electrochemical characteristics were investigated employing Cyclic Voltammetry (CV), Galvanostatic Charge-Discharge (GCD) analysis and Electrochemical Impedance Spectroscopy (EIS). The FTIR spectroscopy confirmed the existence of strong interfacial interaction between NiO and the host matrices showing creation and annihilation of absorption bands in the IR spectra with significant absorptions observed below 500cm-1 for nickel oxide. The TEM results showed that the microstructural evolution of host matrices is as a result of incorporation of NiO and activation using microwave power respectively. A follow-up with XRD confirmed the presence of anomalous graphite structure surrounded by traces of impurities resulting from the activating agent. Finally, the scan rate studies revealed activated palm kernel shell as the best candidate with better current response, higher value of specific capacitance and better electrochemical behaviour

Keywords

Activated carbon nickel oxide microwave activation supercapacitor electrode microstructures electrochemical behaviour Activated carbon nickel oxide microwave activation supercapacitor electrode microstructures electrochemical behaviour

References

  1. Acevedo, B., Barriocanal, C., Lupul, I. and Gryglewicz, G. (2015). Properties and performance of mesoporous activated carbons from scrap tyres, bituminous waste and coal. Fuel, 151: 83-90.
  2. Aravanda, L.S., Bhat, U. and Ramachandra, B. (2013). Binder free MoO3/multi-walled carbon nanotube thin film electrode for high energy density supercapacitor. Electrochim. Acta. 112: 663-669.
  3. Baghbanzadeh, M., Carbone, L., Cozzoli, P.D. and Kappe, C.O. (2011). Microwave-assisted synthesis of colloidal inorganic nanocrystals. Angew, Chemie Int. Ed., 50: 1127-1139.
  4. Bello, A., Barzegar, F., Momodu, D., Taghizadeh, F., Fabiane, M. and Dangbegnon, J. (2014). Morphological characterization and impedance spectroscopy study of porous 3D carbons based on graphene foam-PVA/Phenol-formaldehyde resin composite as an electrode material for supercapacitors. RSC. Adv., 4: 39066-39072.
  5. Conway, C.E. (1999). Electrochemical Supercapacitors: Scientific, Fundamental and Technologcial Applications. Kluwer Academic/Plenum, New York.
  6. Demarconnay, L., Raymundo-Pinero, E. and Beguin, F. (2011). Adjustment of electrodes potential window in an asymmetric Carbon/MnO2 supercapacitor. J. Power Sources, 196: 580-586.
  7. Ge, X., Tian, F., Wu, Z., Yan, Y., Cravotto, G. and Wu, Z. (2015). Adsorption of naphthalene from aqous solution on coal-based active modified by microwave induction: Microwave power effect. Chem. Eng. Process. Process Intensif, 91:67-77.
  8. Halper, M.S. and Ellenbogen, J.C. (2006). Supercapacitors: A brief Overview. MITRE Nanosystems Group: Project no: 15055224, The MITRE Corporation; McLean Virginia, USA.
  9. Jampani, P., Manivannan, A. and Kumta, P.N. (2010). Advancing the supercapacitor materials and technology frontier for improving Power Quality. The Electrochemical Society Interface, Fall 2010.
  10. Kappe, C.O (2008).Microwave dielectric heating in synthetic organic chemistry. Chem. Soc. Rev., 37: 1127-1139.
  11. Markova-Deneva, I. (2010). "Infrared spectroscopy investigation of metallic nanoparticles based on copper, cobalt and nickel synthesized through borohydride reduction method". Journal of the University of Chemical Technology and Metallurgy, 45(4): 351-378.
  12. Mohammadyani, D., Hosseini, S.A. and Sadrnezhaad, S.K. (2012). Characterization of nickel oxide nanoparticles synthesized via rapid microwave-assisted route. International Journal of Modern Physics: Conference Series, 5: 270-276.
  13. Momcilovic, M., Purenovic, M., Bojic, A., Zarabica, A. and Randelovic, M. (2011). Removal of lead (II) ions from aqueous solutions by adsorption onto pine cone activated carbon. Desalination, 276: 53-59.
  14. Nunell, G.V., Fernandenz, M.E., Borelli, P.R. and Cukierman, A.L. (2015). Nitrate uptake improvement by modified activated carbons developed from two species of pine cone. J. Colloid Interface Sci., 440: 102-108.
  15. Ofomaja, A.E. and Naidoo, E. B. (2011). Bisorption of copper from aqueous solution by chemically activated pine cone: A kinetic study. Chem. Eng. J. 175: 260-270.
  16. Park, S., Liang, C., Sheng, D., Dudney, N. and DePaoli, D. (2006). Mesoporous carbon Materials as electrode for electrochemical double layer capacitor. MRS Proc. 973: 903-916.
  17. Roberts, M.E., Wheeler, D.R, McKenzie, B.B. and Bunker, B.C. (2009). High specific capacitance conducting polymer supercapacitor electrodes based on poly [tris(thiophenylphenyl)amine]. J. Mater. Chem., 19: 6977-6979.
  18. Salame, I.I. and Bandosz, T.J. (2001). Surface chemistry of activated carbons: Combining the results of temperature-programmed desorption, boehm and potentiometric titrations. J. Colloid Interface Sci., 240: 252-258.
  19. Taberna, P.L., Simon, P. and Fauvarque, J.-F. F. (2003). Electrochemical characteristics and impedance spectroscopy studies of carbon-Carbon supercapacitors. J. Electrochem. Soc., 150: A292-A300.
  20. Tang, W., Liu, L., Tian, S., Li, L., Yue, Y., Wu, Y. and Zhu, K. (2011). Aqeuos Supercapacitor of High Energy Density based on MoO3 Nanoplates as anode Material. Chem. Commun. 47: 10058-10060.
  21. Wang, H, Casalongue, H.S., Liang, Y. and Dai, H. (2010). Ni(OH)2 nanoplates grown on graphene as advanced electrochemical pseudocapacitor materials. J. Am Chem. Soc. 132: 7472.
  22. Wu, M. -S. and Hsieh, H. -H. (2008). Nickel Oxide/Hydroxide Nanoplate synthesized by chemical precipitation for electrochemical capacitors. Electrochim. Acta., 53: 3427-3435.
  23. Yang, H., Peng, J., Srinivasakannan, C., Zhang, L., Xia, H. and Duan, X. (2010). Preparation of high surface area activated carbon from coconut shells using microwave heating. Biorsour. Technol., 6163-6169.
  24. Zhang, W., Ma, C., Fang, J., Cheng, J., Zhang, X. and Dong, S. (2013). Asymmetric electrochemical capacitors with high energy and power density based on graphene/CoAl-LDH and activated carbon electrodes. RSC. Adv., 3: 2483-2490.
How to Cite

O., A. T., O., O. O., A., G. I., A., S. B., & A., B. (2016). Electrochemical and structural characterization of nickel oxide filled activated carbon for upercapacitor electrode application. Nigerian Journal of Materials Science and Engineering, 7(1), 7-15.

A. T. O., O. O. O., G. I. A., S. B. A., and B. A., "Electrochemical and structural characterization of nickel oxide filled activated carbon for upercapacitor electrode application," Nigerian Journal of Materials Science and Engineering, vol. 7, no. 1, pp. 7-15, June 2016.

Share this article:
Facebook X / Twitter LinkedIn
Download PDF View Full Text (PDF) Back to Articles